microporous bakelite cages ZYS
zys
Home    >     Bearings    >     Engineering plastic cage

Microporous bakelite cage

Technical parameters of Microporous bakelite cages:

 Inner diameter size : Ф25mm~Ф90mm

Outer diameter size : Ф35mm~Ф100mm

Applicable speed : 1000~60000r/min

Applicable temperature : -50~+120℃


Material: Microporous bakelite cage is made of cotton cloth as the base material, phenolic resin as the adhesive, and thermal reactive foaming agent as the pore 

forming agent and then becomes the tubular material after hot rolling and post-curing technology.

Working principle of microporous bakelite cages: After being processed into the cage and immersed in lubricating oil, we can transport the lubricating oil to the cage surface 

by capillary action of cotton fiber, and the controllable lubricating oil can be supplied to the working part of the bearing during bearing operation to achieve high precision 

and long service life of the bearing.


Material grade

Ring  tensile strength/ MPa

Porosity/%

Hole radius/μm

Applicable situation

Microporous bakelite

≥45

10%~20a%

1.0~3.0

Medium and high speed